Failure Analysis of Steel Seal Ring Used in Turbomachinery
Wang, Wenbo
| Autor: | Wang, Wenbo |
|---|---|
| Veröffentlichungsdatum: | 27.05.2017 |
| EAN: | 9783330319424 |
| Sprache: | Englisch |
| Seitenzahl: | 68 |
| Produktart: | Kartoniert / Broschiert |
| Verlag: | LAP LAMBERT Academic Publishing |
Produktinformationen "Failure Analysis of Steel Seal Ring Used in Turbomachinery"
The purpose of this study is to identify the failure cause of the steel seal ring used in nuclear steam turbines. New high nickel steel alloy seal ring was compared with the failed seal ring. Metallographic analysis, scanning electron microscopy, nanoindentation and in-situ tensile testing were used to analyze the reasons of the seal ring failure at both macroscopic and microscopic scales. The main reason of the seal ring failure is a combination of stress and elevated temperature during turbine operation. Complex work environment caused recrystallization and recovery, resulting in grain refinement and secondary phases precipitation. Many secondary phase precipitates appeared at grain boundaries during use, causing formation of microvoids and cracks, ultimately leading to ring failure
Sie möchten lieber vor Ort einkaufen?
Sie haben Fragen zu diesem oder anderen Produkten oder möchten einfach gerne analog im Laden stöbern? Wir sind gerne für Sie da und beraten Sie auch telefonisch.
Juristische Fachbuchhandlung
Georg Blendl
Parcellistraße 5 (Maxburg)
8033 München
Montag - Freitag: 8:15 -18 Uhr
Samstags geschlossen